HOME > About Products > Permanent Antistatic Agents > Grades

Permanent Antistatic Agents

Grades

1.Typical Properties

Select the suitable grades of PELECTRON by referring to the table below.

Product NamePELECTRON HSPELECTRON ASPELECTRON PVL
Appearance Pale yellow pellet Pale yellow pellet Pale yellow pellet
Melting point 135 195 135
Melt flow rate*1 g(10min) 10 30 15
Refractive index 1.50 1.51 1.50
Thermal degradation temp*2 240 285 250
Surface resistivity*3 Ω 4×106 4×106 3×106
Forming method Injection molding Injection molding Extrusion molding
  • *1 Measured according to the method described in ASTM D 1238 (PELECTRON HS and PELECTRON PVL: 190°C, 21.18 N; PELECTRON AS: 215°C, at 21.18 N).
  • *2 The lowest temperature at which PELECTRON begins to thermally decompose.(Measured using a thermal gravimeter in air)
  • *3 PELECTRON itself was molded using an injection molding machine into test pieces, and then the surface resistivity of them was measured using an ultra-megohmmeter at 23°C, 50%R.H.

We offer PELECTRON PVH [MFR (190°C, 21.18N): 6 g (10 min)], a high-viscosity product improvement of PELECTRON PVL.

2. Relation Between Amount of PELECTRON Added and Surface Resistivity

Amount of PELECTRON HS Added to HIPS and Surface Resistivity

Amount of PELECTRON HS Added to PP Resins and Surface Resistivity

Amount of PELECTRON AS Added to ABS Resins and Surface Resistivity

Amount of PELECTRON AS Added to PC/ABS Resins and Surface Resistivity

Amount of PELECTRON PVL Added to PP Resins and Surface Resistivity

Amount of PELECTRON PVL Added to LDPE Resins and Surface Resistivity

Amount of PELECTRON PVL Added to HIPS Resins and Surface Resistivity

3.Influence of PELECTRON on Resin Physical Properties

PELECTRON does not compromise the physical properties of predetermined resins, because this product exhibits high compatibility.

Resin HIPS PP ABS Resin LDPE
PELECTRON HS - HS - AS - PVL -
Amount of PELECTRON Added to Resin wt% 5 0 6 0 10 0 12 0
Forming method Injection molding Extrusion molding
Surface resistivity*1 Ω 3×1010 >1016 3×1011 >1016 8×109 >1016 8×1010 >1016
Melt flow rate*2 g(10min) 13 11 12 10 25 17 3 2
Tensile strength*3 MPa 32 34 15 17 44 46 21 20
Fracture elongation*4 % - - - - - - 590 580
Flexual strength*5 MPa 44 52 29 34 66 70 - -
Flexual modulus*6 MPa 1,890 1,980 1,010 1,200 2,160 2,400 - -
Izod impact strength*7 J/m 100 110 100 110 200 240 - -
Total light transmittance*8 % - - - - - - 86 86
Haze*9 % - - - - - - 34 35
  • *1 ASTM D 257
  • *2 ASTM D 1238 (HIPS: 200°C, 49 N, PP: 230°C, 21.18 N,
    ?ABS resin: 220°C, 98 N, LDPE: 190°C, 21.18 N)
  • *3 ASTM D 638
  • *4 ASTM D 638
  • *5 ASTM D 790
  • *6 ASTM D 790
  • *7 ASTM D 256 (notched)
  • *8 JIS K 7105 (thickness of test pieces: 200 μm)
  • *9 JIS K 7105 (thickness of test pieces: 200 μm)

  