PELESTAT 300

Outline

Polymer-Alloy Type Permanent Antistatic Agent for Polyolefin

Features

· Permanent antistatic agent for polyolefin resins (e.g., polyethylene, polypropylene) which was developed by using an original Sanyo Chemical compatibilization technique.
· This product imparts a permanent antistatic property to polyolefin while causing practically no lowering of their physical properties and moldability. This product dry-blended with polyolefin can be directly molded into the final product, using appropriate molders such as an injection molding machine, an extrusion molding machine and a calender, without a kneading process because this product exhibits excellent dispersibility in polyolefin.
· This product imparts excellent antistatic and antifouling properties (ability to prevent from dust) to polyolefin when the amount added is between 5 and 15 wt %.
· This product exhibits a permanent antistatic property immediately after molding. The antistatic property in the resulting plastic minimally changes even after washing with water because it is a high-molecular-weight antistatic agent. In addition, it works even in low humidity due to its low dependency on humidity.
· This product dry-blended with polyolefin can be directly molded into the final product without a kneading process. Moreover, this product minimally affects the mechanical properties and moldability of the polyolefin.

      

Functions

  • ・Antistatic
     

Applications

  • ・Automobiles
  • ・Electrics/Electronics Parts
  • ・Synthetic Resins & Rubbers
      

Properties, and other information

スクロールできます
Principal Component Polyether-polyolefin block copolymer Appearance Pale yellow pellet Melting Point(℃) 135
Standard Dosage(phr) 5-15(wt %) Applicable resin Polyolefin(Mainly injection molding) Melt flow rate(10min) 30(190℃)(ASTM D 1238(Measured under a load of 21.18N))
Surface Resistivity(Ω) 1×108(ASTM D 257) Thermal degradation temperature(℃) 240(JIS K 7120(TG-DTA, in the air)) Refractive Index 1.49

Precaution Against Mishandling

· In the case of using resins at molding temperatures at 160 ℃ (320 °F), or lower PELESTAT 300 may not fuse, possibly resulting in poor effectiveness. Furthermore, in case of using resins at molding temperatures above 240 ℃ (464 °F), this product may thermally decompose, possibly resulting in poor effectiveness. The recommended molding temperature is between 160 and 230 ℃ (320 – 446 °F).
· Depending on the kind of resin, this product may have an influence on the resin's physical properties such as mechanical properties. Test their influence on each other’s physical properties beforehand to ensure that there are no problems.

      

Other Precautions

Avoid moisture absorption or water stained to protect this product from deterioration.
The color may gradually fade when exposed to light. Also, depending on the storage conditions, etc., it may be colored red in rare cases.

      

Before handling this product, refer to the current Safety Data Sheet for recommended protective equipment, and detailed precautionary and hazards information.If SDS is not listed on the homepage, please contact our sales representative.