PELESTAT HC6800
Outline
Polymer-Alloy Type Permanent Antistatic Agent for Styrene Resins
Features
· Polymer-alloy type permanent antistatic agent for styrene resins which was developed by using an original Sanyo Chemical compatibilization technique.
· This product imparts a permanent antistatic property to styrene resins such as ABS resins and styrene-MMA copolymer (MS resins) while causing practically no lowering of their physical properties and moldability.
· Imparts excellent antistatic property to ABS resin when the additive amount is between 10 and 20 wt %. It prevents from dust (surface resistivity value: the range of 10¹² Ω) and exerts electrostatic dissipative properties to protect electronic parts and circuits (surface resistivity value: the range of 10⁹ Ω).
· Exhibits a permanent antistatic property immediately after molding and the antistatic properties in the resulting plastic remain mostly unchanged even after being washed with water because it is a high-molecular-weight antistatic agent. In addition, it works even in low humidity due to its low dependency on humidity.
· Minimally affects the mechanical properties and moldability of the resins themselves.
· Does not impair the heat resistance of resins because this product is thermally stable.
· Applicable to electric and electronic parts because it contains almost no halogen ions such as chlorine ions or alkali metal ions.
Functions
- ・Antistatic
Applications
- ・Automobiles
- ・Electrics/Electronics Parts
- ・Synthetic Resins & Rubbers
Properties, and other information
| Principal Component | Polyether-ester-amide block copolymer | Appearance | Pale yellow pellet | Melting Point（℃） | Approx. 199 °C (390 °F) |
| Melt flow rate（10min） | 約 30ｇ（10min）［ASTM D 1238（215℃、21.18N）］ | Surface Resistivity（Ω） | 約３×107 Ω （ASTM D 257） | Thermal degradation temperature（℃） | Approx. 285 °C (545 °F)／（JIS K 7120（TG-DTA, in the air）） |
| Reduced Viscosity | 1.7（0.5 wt % formic acid solution at 25℃） | Refractive Index | 1.51 ［ASTM D 542（23℃）］ |
Precaution Against Mishandling
· In the case of using resins at molding temperatures at 200 ℃ (392 °F) or lower, PELESTAT HC6800 may not fuse, possibly resulting in poor effectiveness. Furthermore, in case of using resins at molding temperatures above 300 ℃ (572 °F), this product may thermally decompose, possibly resulting in poor effectiveness.
· Depending on the kind of resin, this product may have an influence on the resin's physical properties such as mechanical properties. Test their influence on each other’s physical properties beforehand to ensure that there are no problems.
Other Precautions
Avoid moisture absorption or water stained to protect this product from deterioration.
The color may gradually fade when exposed to light. Also, depending on the storage conditions, etc., it may be colored red in rare cases.
Before handling this product, refer to the current Safety Data Sheet for recommended protective equipment, and detailed precautionary and hazards information.If SDS is not listed on the homepage, please contact our sales representative.