PELECTRON PVL
Outline
Polymer-Alloy Type Permanent Antistatic Agent for Polyolefin (Low-Resistivity)
Features
· Polymer-alloy type permanent antistatic agent for polyolefin resins (e.g., polyethylene, and polypropylene) which was developed by using an original Sanyo Chemical compatibilization technique.
· This product imparts a long-lasting antistatic property to polyolefin resins as well as causing practically no degradation of their physical properties and moldability. This product dry-blended with polyolefin can be directly molded without a kneading process because this product exhibits excellent dispersibility in polyolefin. In addition, compared to conventional permanent antistatic agents, PELECTRON PVL exhibits an excellent antistatic property even when used in small amounts because this product substantially decreases surface resistivity of polyolefin.
· Imparts an excellent antistatic property (the ability to prevent problems such as dust and electrostatic faults) to polyolefin when the additive amount is between 5 and 20 wt %.
· Imparts an excellent antistatic property to polyethylene and polypropylene for films and sheets as well as causing practically no lowering of their physical properties.
· Exhibits a long-lasting antistatic property immediately after molding and the antistatic properties in the resulting plastic remain mostly unchanged even after being washed with water because it is a high-molecular-weight antistatic agent. In addition, it works even in low humidity due to its low dependency on humidity.
· This product dry-blended with polyolefin can be directly molded without a kneading process because this product exhibits excellent dispersibility in polyolefin.
Functions
- ・Antistatic
Applications
- ・Automobiles
- ・Electrics/Electronics Parts
- ・Synthetic Resins & Rubbers
Properties, and other information
| Principal Component | Polyether-polyolefin block copolymer | Appearance | Pale yellow pellet | Melting Point（℃） | 135 |
| Standard Dosage（phr） | 5-20（wt %） | Applicable resin | Polyolefin（Mainly injection molding） | Melt flow rate（10min） | 15（190℃）（ASTM D 1238（Measured under a load of 21.18N）） |
| Surface Resistivity（Ω） | 3×106（ASTM D 257） | Thermal degradation temperature（℃） | 250（JIS K 7120（TG-DTA, in the air）） |
Precaution Against Mishandling
· In the case of using PELECTRON PVL at molding temperatures below 170 ℃ (338 °F), this product may not fuse, resulting in poor effectiveness. Furthermore, in case of using PELECTRON PVL at molding temperatures above 240 ℃ (464 °F), this product may thermally decompose, resulting in poor effectiveness. The recommended molding temperature is between 170 and 230 ℃ (338 – 446 °F).
· Depending on the kind of resin, this product may have a negative effect on the resin's physical properties including mechanical properties. Test the effects on each of the physical properties beforehand to ensure that there are no problems.
Other Precautions
Avoid moisture absorption or water stained to protect this product from deterioration.
The color may gradually fade when exposed to light. Also, depending on the storage conditions,etc., it may be colored red in rare cases.
Before handling this product, refer to the current Safety Data Sheet for recommended protective equipment, and detailed precautionary and hazards information.If SDS is not listed on the homepage, please contact our sales representative.